Ceramic Fiber Module
Ceramic Fiber Module
Ceramic Fiber Module is made of blanket fan folded, or pre-cut blanket stack bonded to form a module, to form a module with cut edges exposed.
CHARACTERISTIC
Low density and low thermal conductivity
To be secured by concealed anchor
Greater mechanical strength
Shorter heat up and cool down time
Resilience and resistance to thermal shock
Flexible and easy to cut or install
-
Asbestos free
APPLICATIONS
High gas flow velocity furnace or duct lining
-
Direct exposure to heat as furnace hot face lining
TECHNICAL DATA
Blanket Product |
MCF1050 |
MCF1260ST |
MCF1260HP |
MCF1300HA |
MCF1300LAZS |
MCF1430AZS |
Temperature Grade°C |
1050 |
1260 |
1260 |
1300 |
1300 |
1430 |
Recommended Operation Temperature°C |
≤950 |
≤1100 |
≤1150 |
≤1200 |
≤1200 |
≤1250 |
Product Code |
MYTX-PT-02 |
MYTX-BZ-02 |
MYTX-GC-02 |
MYTX-GL-02 |
MYTX-DG-02 |
MYTX-HG-02 |
Permanent Linear Shrinkage (%) |
950°C×24h≤4 |
1000°C×24h≤4 |
1100°C×24h≤4 |
1200°C×24h≤4 |
1250°C×24h≤4 |
1350°C×24h≤4 |
Nominal Density (kg/m3) |
180~240 |
|||||
Al2O3 |
≥40 |
≥43 |
≥44 |
≥52 |
||
Al2O3+SiO2 |
≥95 |
≥97 |
≥98.5 |
≥98.5 |
||
Al2O3+SiO2+ZrO2 |
- |
- |
≥99 |
≥99 |
||
ZrO2 |
- |
- |
5~7 |
≥15 |
||
Fe2O3 |
≤1.0 |
≤1.0 |
≤1.0
|
≤1.0
|
≤0.5 |
≤0.5 |
Availability (mm) |
Per customer’s drawing |
|||||
Note: Test data shown are average results of tests conducted under standard procedures and are subject to variation. Results should not be used for specification purpose. The product is listed comply to ASTM C892.